Heat Treatment Forged Steel Bar SCM445 / 50CrMo4 / Din 1.7228 / 4145 Alloy Steel

کیفیت خوب فولاد لوله های سرد ساخته شده است برای فروش
کیفیت خوب فولاد لوله های سرد ساخته شده است برای فروش
چت IM آنلاین در حال حاضر

Heat Treatment Forged Steel Bar SCM445 / 50CrMo4 / Din 1.7228 / 4145 Alloy Steel

چین Heat Treatment Forged Steel Bar SCM445 / 50CrMo4 / Din 1.7228 / 4145 Alloy Steel تامین کننده
Heat Treatment Forged Steel Bar SCM445 / 50CrMo4 / Din 1.7228 / 4145 Alloy Steel تامین کننده Heat Treatment Forged Steel Bar SCM445 / 50CrMo4 / Din 1.7228 / 4145 Alloy Steel تامین کننده Heat Treatment Forged Steel Bar SCM445 / 50CrMo4 / Din 1.7228 / 4145 Alloy Steel تامین کننده Heat Treatment Forged Steel Bar SCM445 / 50CrMo4 / Din 1.7228 / 4145 Alloy Steel تامین کننده

تصویر بزرگ :  Heat Treatment Forged Steel Bar SCM445 / 50CrMo4 / Din 1.7228 / 4145 Alloy Steel

جزئیات محصول:

Place of Origin: China
نام تجاری: UST
گواهی: ISO9001
Model Number: DIA80-1200mm

پرداخت:

Minimum Order Quantity: MOQ: 3tons
قیمت: FOB USD 800- 900/ton
Packaging Details: Plastic plugs in both ends, Hexagonal bundles of max 2,000kg with several steel strips, Two tags on each bundle, Wrapped in waterproof paper, PVC sleeve, and sackcloth with several steel strips.
Delivery Time: Within 10-45 days
Payment Terms: L/C, T/T
Supply Ability: 1500 ton/month
Contact Now
توضیحات محصول جزئیات
Process:: hot forged+heat treatment surface: Black or Bright
ISO: 9001-2008 Ultrasonic test: According to SEP 1921-84
Inspection: the third party is acceptable material: alloy steel bar

SCM445 /50CrMo4/din 1.7228/4145 hot forged steel price per kg, forged steel bar, Small MOQ

 

Applications

 

AISI 4145H MOD Steel is a chromium molybdenum alloy steel grade widely used in the oil and gas sectors. Similar to AISI 4140 but with a higher carbon content. AISI 4145H MOD Steel is more popular in larger diameters due to its increased strength and harden-ability. AISI 4145H MOD Steel is commonly supplied quenched and tempered with a hardness of between 30 to 36HRc. AISI 4145H MOD Steel is commonly used for a variety of applications in the oil and gas sector. Used often for the manufacture of down hole drilling tools such as drill collars. Other applications include gears, shafts for hydraulic presses, rolls for paper mills, pump shafts and tool holders.

Quality Standard

ASTM A29 Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought, General
API 7 Specification for Rotary Drill Stem Elements.

 

Chemical Composition (%)

 

C: 0.42-0.49

Mn: 0.65-1.1

Si: 0.15-0.35

Cr:0.75-1.2

Mo:0.15-0.25

 

METALLURGICAL CONDITIONS

 

Grain Size: The austenitic grain size shall be 6-9 as defined in ASTM E-112.

 

Process: EAF+LF+VOD+Forged+Heat Treatment(optional)

HEAT TREATMENT

Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of eachAISI 4145H MOD Steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult your heat treatment provider for full guidance on heat treatment of AISI 4145H MOD Steel.
Annealing: Heat the steel slowly to 800-850°C and allow enough time for the steel to be thoroughly heated. Cool slowly in the furnace to 480°C followed by air cooling.
Stress Relieving: When parts are heavily machined, ground or otherwise subject to cold work, stress relieving will be beneficial prior to hardening.
Hardening: AISI 4145H MOD Steel is usually supplied ready heat treated to 30-36HRc. If further heat treatment is required annealed AISI 4145H MOD Steel should be heated slowly to 840-875°C and after adequate soaking at this temperature quench in oil. Temper as soon as the tools reach room temperature.
Tempering: Heat carefully to a suitable temperature selected by reference to a tempering chart or table (usually between 550-700°C, soak at the temperature for 2 hours per 25mm of ruling section, then allow to cool in air. Tempering between 250-375°C is not advised as tempering within this range will seriously reduce the impact values of this steel.

 

 

SIZE RANGE:

Round:

Hot Forged: 80mm -1200mm

 

SURFACE FINISHES:

Black, Peeled (K12), Turned & Polished (H10, H11),

 

Test: Ultrasonic test according to SEP 1921-84

 

Product Description

steel price per kg AISI4145Hsteel price per kg AISI4145Hsteel price per kg AISI4145H

اطلاعات تماس
SHANGHAI UNITE STEEL TRADING CO., LTD

تماس با شخص: Anndy

تلفن: +8615502127172

ارسال درخواست خود را به طور مستقیم به ما (0 / 3000)